Qattiq jismlarning siqiluvchanligi.
Jadvalda bazi qattiq jismlarning 20 C harorat va 10 50 MPa (?100 500 atm) bosim diapazonidagi ortacha izotermik siqiluvchanlik koefitsienti[1] - k ning qiymatlari keltirilgan.
|
Qattiq jism |
k, 110-1 Pa |
Qattiq jism |
k, 110-1 Pa |
Qattiq jism |
k, 110-1 Pa |
|
Alyuminiy |
1.4 |
Magniy |
2.8 |
Platina |
0.4 |
|
Fosfor oq |
20.5 |
Marganets |
0.9 |
Qalay |
1.9 |
|
Fosfor qizil |
9.2 |
Mis |
0.7 |
Qo'rg'oshin |
2.3 |
|
Grafit |
3.0 |
Molibden |
0.5 |
Rux |
1.7 |
|
Kaliy |
32.0 |
Natriy |
15.8 |
Seziy |
62.0 |
|
Kaltsiy |
5.8 |
Nikel |
0.5 |
Shisha |
2.1 |
|
Kremniy |
0.3 |
Olmos |
0.2 |
Temir |
0.6 |
|
Kumush |
1.0 |
Oltin |
0.6 |
Vismut |
3.0 |
|
Litiy |
9.0 |
Oltingugurt |
13.0 |
Volfram |
0.3 |
|
Xrom |
0.9 |
||||
[1] Siqiluvchanlik koefitsienti k , bosimning 1 Pa ga ortishida jismning hajmining kamayish ulushi miqdori.